YINSHAN 42.5 Highest quality for sulphoaliminate cement 42.5/Low Alkalinity Cement

Short Description:

Fast setting
High early strength (3-day strength equals the 28-day strength of ordinary cement)
Continuous strength development (no loss of strength in time)
Rapid drying (C4A3Š autogenously binds excess water)
Shrinkage compensated – (little to NO shrinkage)
Low alkali PH<10.5
Good frost resistance/Impermeability/carbonization resistance/corrosion resistance.


Product Detail

Product Tags

Application

advanced packing machine

White CSA cement is a special Calcium Sulfo Aluminate cement (CSA) designed for decorative concrete, terrazzo, flooring, glass fiber reinforced concrete (GFRC), dry-mixed mortars, non-shrink grout architectural precast, fiber cement and more. Specially selected high purity raw materials, optimized calcination and carefully monitored grinding guarantee a consistent white color.
Certified Product Manufactured under GB/T 19001-2008 IDT ISO9001:2008 Quality Management System.

Specification

 

Chemical parameter analysis
SiO2 7.81
Al2O3 37.31
Fe2O3 0.14
CaO 40.78
MgO 0.37
SO3 11.89
f-CaO 0.07%
Loss 0.29
Physical parameter analysis
Blaine finenes(cm2/g) 4500
Setting time(min) Initial (min)≥ 15 Based on customer request
Final≤ 120
Compress strength(Mpa) 6h 25
1d 55
3d 65
28d 72
Flexural strength(Mpa) 6h 6.0
1d 9.0
3d 10.0
28d 11.0
Whiteness (hunter) Over 91%

Benefits

1. Fast setting, Rapid hardening, high strength; 4h compressive strength can reach 15 Mpa, 43 Mpa after 28d,suitable to make the high strength products.
2. Micro expansion, low dry shrinkage, the length change is very small. Dry shrinkage rate is just 1/10 of Portlandcement.
3. Have very good anti-corrosion property in sulfate, chloride, magnesium salt and seawater. Corrosion resis.
tance coefficient >1.
4. High impermeability, permeation height is 1/5 of Portland cement.
5. High frozen resistance property, can get the strength of critical intensity of cold in 2h~3h.
6. Low hydration heat release
7. PH value is under 10.0 for GRC products.
9. Whiskering resistant performance is good10. Can be mixed with Portland cement in a proper ratio, can greatly reduce the shrinkage of Portland cement,reduce the cracks.

Suitable projects include

 

1.GRC
2.Decoratlon mortar
3. lnterior and exterior wall putty4. indoor and outdoor fioer
5. Cement-based self-leveling mortar
6. Artificial stone and floor
7. Thin layer of concrete repair and concrete leveling material
8.Anti-cracking rending mortar
9. Exterior insulation rendering mortar, bonding mortar and tile adhesive
10.Decorative concrete
11.Prefabricated concrete
12.Building reinforcement
13. High early strength Non-shrinkage grouts
14.Waterproof and plugging material

Zero to Low Shrinkage

CSA cement achieves higher early strength than portlandcement allowing for the formulation of non-shrink and low-shrinkage concrete and mortar products. CSA cement utilizes nearly 100% of the mix water during hydration process, leaving very little water to contribute towards shrinkage. Hydration temperature is considerable lower than comparable quick setting systems .Additionally, because of high early strength development, little or no shrinkage occurs after initial set.